Silicon-Nanowire Transistors with Intruded Nickel-Silicide Contacts

Schottky barrier field effect transistors based on individual catalytically-grown and undoped Si-nanowires (NW) have been fabricated and characterized with respect to their gate lengths. The gate length was shortened by the axial, self-aligned formation of nickel-silicide source and drain segments along the NW. The transistors with 10−30 nm NW diameters displayed p-type behaviour, sustained current densities of up to 0.5 MA/cm2, and exhibited on/off current ratios of up to 107. The on-currents were limited and kept constant by the Schottky contacts for gate lengths below 1 μm, and decreased exponentially for gate lengths exceeding 1 μm.      «

Schottky barrier field effect transistors based on individual catalytically-grown and undoped Si-nanowires (NW) have been fabricated and characterized with respect to their gate lengths. The gate length was shortened by the axial, self-aligned formation of nickel-silicide source and drain segments along the NW. The transistors with 10−30 nm NW diameters displayed p-type behaviour, sustained current densities of up to 0.5 MA/cm2, and exhibited on/off current ratios of up to 107. The on-currents w...     »