{{HT}}-Solution Growth and Characterisation of {{InxNaxMn1}}-{{2xWO4}} (0

Dokumenttyp:
Zeitschriftenaufsatz
Autor(en):
Gattermann, U.; Park, S. -H.; Paulmann, C.; Benka, G.; Pfleiderer, C.
Abstract:
A new solid solution system, InxNaxMn1\textendash{}2xWO4 (0$<$x=$\leq$0.26) belonging to the MnWO4-type multiferroics was investigated. Large single crystals were grown up to several mm in length from high-temperature oxide solutions using a solvent mixture of Na2WO4 and Na2W2O7. Quantitative doping degrees were analyzed by means of electron microprobe. Single crystal X-ray diffraction studies agreed with the polar space group P2 for InxNaxMn1\textendash{}2xWO4. The complexity of partial (Na+/Mn2+)- and (In3+/Mn2+)-ordering makes their atomic sites unique, explaining the dissymmetrization from P2/c down to P2. This is also valid for the InNaW2O8-type Mn2yIn1-yNa1-yW2O8 solid solution found as co-product in this study. Specific heat and magnetisation measurements showed a paramagnetic dilution effect from (In3+/Na+)-doping while lowering the transition temperature for the multiferroic phase AF2 of InxNaxMn1\textendash{}2xWO4 with respect to the prototype MnWO4.
Stichworte:
(In/Na)-doping,Magnetization,MnWO,Multiferroics,Polar structure,X-ray diffraction
Zeitschriftentitel:
Journal of Solid State Chemistry
Jahr:
2016
Band / Volume:
244
Monat:
dec
Seitenangaben Beitrag:
140
Volltext / DOI:
doi:10.1016/j.jssc.2016.09.022
Print-ISSN:
0022-4596
 BibTeX