Temperature Compensation of Solidly Mounted Bulk Acoustic Wave Resonators
Übersetzter Titel:
Temperaturkompensation von Solidly-mounted Bulk Acoustic Wave Resonatoren
Autor:
Abd Allah, Mohamed Hassan Ahmed
Jahr:
2010
Dokumenttyp:
Dissertation
Fakultät/School:
Fakultät für Elektrotechnik und Informationstechnik
Betreuer:
Prof. Dr. rer. nat. Doris Schmitt-Landsiedel
Sprache:
en
Fachgebiet:
ELT Elektrotechnik
TU-Systematik:
ELT 770f
Kurzfassung:
This thesis introduces a novel way of temperature compensation of Bulk Acoustic Wave (BAW) resonators. By adding very thin (30-70nm) SiO2 layers at high stress regions within the resonator, temperature coefficients ranging from -10 ppm/˚C to +12ppm/˚C have been successfully demonstrated. With this method, it was possible to reach full temperature compensation of less than 1ppm/˚C with the use of only 32nm placed within 1180 nm of AlN. Thanks to this significant reduction in SiO2 thickness, more...     »
Übersetzte Kurzfassung:
Die Arbeit stellt eine neue Methode zur Temperatur-Kompensation von Bulk Acoustic Wave (BAW) Resonatoren vor. Durch Einbringung von sehr dünnen (30-70-nm) SiO2-Schichten in Bereiche hoher Druckbelastung innerhalb des Resonators wurden Temperaturkoeffizienten von -10 ppm /˚C bis +12 ppm /˚C erreicht. Mit einer Schicht von nur 32 nm in 1180 nm AlN konnte eine vollständige Temperaturkompensation bei weniger als 1 ppm / ˚ C erzielt werden. Dank dieser deutlichen Reduzierung der SiO2-Dicke gegenüber...     »