Surface modifications on lithium-ion-battery cell components 
Translated title:
Oberflächenbeeinflussung von Zellkomponenten in Lithium-Ionen-Batterien 
Year:
2021 
Document type:
Dissertation 
Institution:
Fakultät für Chemie 
Advisor:
Gasteiger, Hubert A. (Prof. Dr.) 
Referee:
Gasteiger, Hubert A. (Prof. Dr.); Pettinger, Karl-Heinz (Prof. Dr.) 
Language:
en 
Subject group:
CHE Chemie; CIT Chemie-Ingenieurwesen, Technische Chemie, Biotechnologie 
Keywords:
Lithium-Ion-Battery, Electrochemical Impedance Spectroscopy, Neutron Depth Profiling, Lamination, Formation, Solid-Electrolyte-Interface, Lifetime, Fast-Charging 
Translated keywords:
Lithium-Ionen-Batterie, Elektrochemische Impedanzspektroskopie, Neutron Depth Profiling, Lamination, Formierung, Solid-Electrolyte-Interface, Schnell-Laden 
TUM classification:
CHE 140; CIT 335 
Abstract:
The electrode-separator lamination technique is demonstrated to significantly improve C-rate stability, fast-charging capability and the fast-formation stability of graphite-NMC 111 cells. Electrochemical Impedance Spectroscopy was used to separate lamination effects between anode separator and cathode-separator interfaces, which were found to either reduce aging effects or internal resistances. Neutron-Depth-Profiling was used for determination of changes in anodic SEI growth characteristics. 
Translated abstract:
Anhand von Graphit-NMC 111 Zellen wurden positive Einflüsse der Prozesstechnologie Lamination auf Ratenfestigkeit, Schnell-Lade-Verhalten sowie die Schnell-Formierbarkeit untersucht. Mit elektrochemischer Impedanzspektroskopie wurden Unterschiede der anoden- und kathodenseitigen Lamination untersucht, die jeweils entweder Alterungseffekte oder Innenwiderstände beeinflussen. Durch Neutron-Depth-Profiling wurden Einflüsse auf das anodische SEI Wachstum ermittelt. 