Core-shell nanocatalyst activities are chiefly controlled by bimetallic material composition, shell thickness, and nanoparticle size. We present a machine learning framework predicting strain with site-specific precision to rationalize how strain on Pt core-shell nanocatalysts can enhance oxygen reduction activities. Large compressive strain on Pt@Cu and Pt@Ni induces optimal mass activities at 1.9 nm nanoparticle size. It is predicted that bimetallic Pt@Au and Pt@Ag have best mass activities at 2.8 nm, where active sites are exposed to weak compressive strain. We demonstrate that optimal strain depends on the nanoparticle size: for instance, strengthening compressive strain on 1.92 nm sized Pt@Cu and Pt@Ni, or weakening compressive strain on 2.83 nm sized Pt@Ag and Pt@Au, can lead to further enhanced mass activities.     «

Core-shell nanocatalyst activities are chiefly controlled by bimetallic material composition, shell thickness, and nanoparticle size. We present a machine learning framework predicting strain with site-specific precision to rationalize how strain on Pt core-shell nanocatalysts can enhance oxygen reduction activities. Large compressive strain on Pt@Cu and Pt@Ni induces optimal mass activities at 1.9 nm nanoparticle size. It is predicted that bimetallic Pt@Au and Pt@Ag have best mass activities at...     »