In this work, the biocompatibility of titanium before and after oxygen PIII is investigated using a rat animal model. Pure titanium (grade 2) and pre-anodized titanium were implanted with oxygen at elevated temperatures between 200 and 550 degreesC and subsequently analyzed for oxygen content and phase composition. No deterioration of the tensile strength and the yield strength was detected after the implantation. The mechanical stability of the osseointegration was determined with a pull-out test, where an increased shear strength was measured after PIII treatment. Only a slight improvement of the bone contact area, from an already excellent starting value, was observed for pure titanium. In contrast, a significant improvement was found for anodized titanium after PIII treatment. This astonishing difference can be explained with the surface topography and the phase composition of the anodized titanium samples. (C) 2003 Elsevier Science B.V. All rights reserved.     «

In this work, the biocompatibility of titanium before and after oxygen PIII is investigated using a rat animal model. Pure titanium (grade 2) and pre-anodized titanium were implanted with oxygen at elevated temperatures between 200 and 550 degreesC and subsequently analyzed for oxygen content and phase composition. No deterioration of the tensile strength and the yield strength was detected after the implantation. The mechanical stability of the osseointegration was determined with a pull-out te...     »